Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelAISI 347H plate,AISI 347H Round Bar,AISI 347H forgings,AISI 347H suppliers, AISI 347H Stock,AISI 347H sheet, AISI 347H flat bar, AISI 347H pipe,AISI 347H tube,AISI 347H mould,AISI 347H round ingot,AISI 347H cold-rolled steel,AISI 347H coil,AISI 347H strap steel,AISI 347H hot-rolled steel,AISI 347H medium plate, AISI 347H heavy plate,AISI 347H shapped bar,AISI 347H hexahedral bar,AISI 347H,AISI 347H slab ingot,AISI 347H slab,AISI 347H price,AISI 347H square bar,AISI 347H square steel,AISI 347H wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 347H.

Current Location:Home » Products » Stainless Steel » AISI 347H

Product category

AISI 347H

Data Table for:Products: Stainless Steel:AISI 347H

AISI 347H properties and heat treatment forged piece, Including AISI 347H application and specifications, We have all specifications,Including AISI 347H steel plate, AISI 347H sheet, AISI 347H square steel, AISI 347H flat bar,AISI 347H round bar,AISI 347H forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 347H has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 347H and Standards

C(%): 0.04~0.10
Si(%): ≤1.00
Mn(%): ≤2.00
P(%)≤: 0.04
S(%)≤: 0.03
Cr(%): 17.0~20.0
Ni(%): 9.00~13.0
Mo(%): —
8×C≤Nb/Ta≤1.10




Machining performance

Download AISI 347H the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.