Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless Steel430f plate,430f Round Bar,430f forgings,430f suppliers, 430f Stock,430f sheet, 430f flat bar, 430f pipe,430f tube,430f mould,430f round ingot,430f cold-rolled steel,430f coil,430f strap steel,430f hot-rolled steel,430f medium plate, 430f heavy plate,430f shapped bar,430f hexahedral bar,430f,430f slab ingot,430f slab,430f price,430f square bar,430f square steel,430f wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 430f.

Current Location:Home » Products » Stainless Steel » 430f

Product category

430f

Data Table for:Products: Stainless Steel:430f

430f properties and heat treatment forged piece, Including 430f application and specifications, We have all specifications,Including 430f steel plate, 430f sheet, 430f square steel, 430f flat bar,430f round bar,430f forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 430f has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 430f and Standards

Stainless Steel
AISI 430F Stainless Steel

Designations
France: AFNOR Z 10 CF 17
Germany: DIN 1.4104
Italy: UNI x 10 CrS 17
Japan: JIS SUS 430
Sweden: SS 2383
United States: ASTM A314 , ASTM A473 , ASTM A581 , ASTM A582 , MIL SPEC MIL-S-862 , SAE 51430F , SAE J405 (51430F) , UNS S43020

Chemical Composition

Element
Weight %
C
 0.12 
Mn
 1.25 
Si
 1.00 
Cr
 16.0-18.0 
P
 0.06 
S
 0.15 (min) 
Mo(optional)
 0.6 

Mechanical Properties

Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.8
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
200
25
 
Tensile Strength (Mpa)
722.5 
25 
annealed (wire) 
Yield Strength (Mpa)
105 
Elongation (%)
 
Reduction in Area (%)
 

Thermal Properties

Properties
 Conditions 
T (°C)
Treatment
Thermal Expansion (10-6/ºC)
10.4 
0-100 
 
Thermal Conductivity (W/m-K)
26.1 
100
 
Specific Heat (J/kg-K)
460 
0-100 
 

Electric Properties

Properties
 Conditions 
T (°C)
Treatment
Electric Resistivity (10-9W-m)
600 
25 
 




Machining performance

Download 430f the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.