Our to produce better steel-based products are the main used in industrial manufacturing various types Mould steel347 plate,347 Round Bar,347 forgings,347 suppliers, 347 Stock,347 sheet, 347 flat bar, 347 pipe,347 tube,347 mould,347 round ingot,347 cold-rolled steel,347 coil,347 strap steel,347 hot-rolled steel,347 medium plate, 347 heavy plate,347 shapped bar,347 hexahedral bar,347,347 slab ingot,347 slab,347 price,347 square bar,347 square steel,347 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 347.

Current Location:Home » Products » Mould steel » 347

Product category

347

Data Table for:Products: Mould steel:347

347 properties and heat treatment forged piece, Including 347 application and specifications, We have all specifications,Including 347 steel plate, 347 sheet, 347 square steel, 347 flat bar,347 round bar,347 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 347 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 347 and Standards

Detailed Product Description

High-quality Hot Working Mould steel.
We have the absolute price advantage and technological advantages.           
           
Rich in power resources and strong technical force, so that our special steel products have the absolute price
advantage and technological superiority.
Forged/Hot rolled steel: Round bar/Square bar/Plate/Coil/Wire/Forging
Size:
Round Bar: Dia 1mm to 2000mm
quardrant iron, square bar iron, square steel : Dia 30mm to 600mm
Flat/Plate: Thickness: 0.5mm to 700mm
Width: 20mm to 2000mm
Length: According to client's requirements.
Forging  or rolled steel : Step Shaft/Tube/Pie-shaped/Ring/Module/Large valves of the main/Other Profiled Forgings


Delivery Condition: Hot Forged/Hot rolled + Annealing/Normalizing/Tempering/Quenching and
tempering/Solution/Aging/Slow Cooling
Surface Quality: Black Surface/Grinding Surface/Roughing/Finish Machining
Smelting Process: EAF+LF+VD(+ESR)+vacuum arc melting furnace
Ultrasonic Test: According to the customer's technical standards to ensure pass the ultrasonic flaw detection.
We do hope the regular trade relations can be established between us.With our joint efforts, we believe trade
between us will surely develop fast and to our mutual benefit.
If there is any question or suggestion, please don't hesitate to tell us.We shall be pleased to make efforts to meet
your requirements.
We are expecting cooperating with you sincerely and tightly details will be checked when firm inquiry.




Machining performance

Download 347 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:347 steel plate, 347 sheet, 347 square steel, 347 flat bar,347 round bar,347 forgings