304S11 properties and heat treatment forged piece, Including 304S11 application and specifications, We have all specifications，Including 304S11 steel plate, 304S11 sheet, 304S11 square steel, 304S11 flat bar,304S11 round bar,304S11 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the 304S11 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade 304S11 and Standards
Introduces basic
Chemical composition
Carbon C: more than 0.030
Si: more than 1.00 silicon
Manganese Mn: more than 2.00
P: more than 0.040 P
S: more than 0.030 sulfur
Chromium Cr: 17.00 ~ 19.00
Mo: avoid measurement molybdenum
Ni Ni: 9.00 ~ 12.00
Copper Cu: avoid measurement
Other: avoid measurement
Third, physical properties
304 S11 Physical properties of the Physical properties
S11 tensile test: 304
Steel thickness (mm) : from the point of measuring the yield point yield (MPa) sigma s: acuity 215 tensile strength tensile strength (MPa) sigma b: 480 ~ 680
Steel thickness (mm) : from the point of measuring the yield point yield (MPa) sigma s: avoid measure tensile strength tensile strength (MPa) sigma b: avoid measurement
Four, material cross-references
304 S11 material that will offer an Products of the table
Reference standard standard instead:
China GB13296-91 Cr19Ni9
Material that will offer an Products: table
China GB13296-91 Cr19Ni9
Japan JIS G3463-94 SUS304LTB
The United States ASTM A213M-94 bASTM A249M-94 aASTM A269-94 bASTM A632-90-91 A688M ASTM TP304L TP304L TP304L TP304L TP304L
British BS3605Part1-1991-1992 304 304 BS3606 S11 S51
German DIN 17457 85 DIN 17458 85 X2CrNi1911 X2CrNi1911
The French NF A49 217:1987 TUZ2CN18 10
ISO ISO 2604 out of the 75 TS 46
Five, the price
304-304 S11 Suppliers S11 supplier price
Six, production process
304 S11 Production process Production mode
Seven, characteristic USES
304 S11 characteristics USES Features assumptions
Eight, heat treatment process
304 S11 Heat treatment of Heat treatment process
Machining performance
Download 304S11 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.