Our to produce better steel-based products are the main used in industrial manufacturing various types Mould steel2Cr12MoV plate,2Cr12MoV Round Bar,2Cr12MoV forgings,2Cr12MoV suppliers, 2Cr12MoV Stock,2Cr12MoV sheet, 2Cr12MoV flat bar, 2Cr12MoV pipe,2Cr12MoV tube,2Cr12MoV mould,2Cr12MoV round ingot,2Cr12MoV cold-rolled steel,2Cr12MoV coil,2Cr12MoV strap steel,2Cr12MoV hot-rolled steel,2Cr12MoV medium plate, 2Cr12MoV heavy plate,2Cr12MoV shapped bar,2Cr12MoV hexahedral bar,2Cr12MoV,2Cr12MoV slab ingot,2Cr12MoV slab,2Cr12MoV price,2Cr12MoV square bar,2Cr12MoV square steel,2Cr12MoV wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 2Cr12MoV.

Current Location:Home » Products » Mould steel » 2Cr12MoV

Product category

2Cr12MoV

Data Table for:Products: Mould steel:2Cr12MoV

2Cr12MoV properties and heat treatment forged piece, Including 2Cr12MoV application and specifications, We have all specifications,Including 2Cr12MoV steel plate, 2Cr12MoV sheet, 2Cr12MoV square steel, 2Cr12MoV flat bar,2Cr12MoV round bar,2Cr12MoV forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 2Cr12MoV has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 2Cr12MoV and Standards

Step Shaft 2Cr12MoV Tube 2Cr12MoV Pie-shaped 2Cr12MoV Ring 2Cr12MoV Module 2Cr12MoV Large valves of the main 2Cr12MoV Other Profiled Forgings 2Cr12MoV

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.




Machining performance

Download 2Cr12MoV the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:2Cr12MoV steel plate, 2Cr12MoV sheet, 2Cr12MoV square steel, 2Cr12MoV flat bar,2Cr12MoV round bar,2Cr12MoV forgings