Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless Steel1.6368 plate,1.6368 Round Bar,1.6368 forgings,1.6368 suppliers, 1.6368 Stock,1.6368 sheet, 1.6368 flat bar, 1.6368 pipe,1.6368 tube,1.6368 mould,1.6368 round ingot,1.6368 cold-rolled steel,1.6368 coil,1.6368 strap steel,1.6368 hot-rolled steel,1.6368 medium plate, 1.6368 heavy plate,1.6368 shapped bar,1.6368 hexahedral bar,1.6368,1.6368 slab ingot,1.6368 slab,1.6368 price,1.6368 square bar,1.6368 square steel,1.6368 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.6368.

Current Location:Home » Products » Stainless Steel » 1.6368

Product category

1.6368

Data Table for:Products: Stainless Steel:1.6368

1.6368 properties and heat treatment forged piece, Including 1.6368 application and specifications, We have all specifications,Including 1.6368 steel plate, 1.6368 sheet, 1.6368 square steel, 1.6368 flat bar,1.6368 round bar,1.6368 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.6368 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.6368 and Standards

steel name: 1.6368
  steel names of producers:
  NiCuMoNb5-6-4 DIN EN 10028-2:2003-09 Germany
  NiCuMoNb5-6-4 DIN EN 10216-2:2007-10 Germany
  NiCuMoNb5-6-4 Stahl Eisen List: 2004 Germany
  NiCuMoNb5 SEW 028:1993-05 Germany
  DIWA373 Dillinger Hüttenwerke Germany
  WB36 HKM Krupp Mannesmann Germany
  NiCuMoNb5 Hover&Sohn Germany
  NiCuMoNb5 Saarstahl Germany
  NiCuMoNb5-6-4 DIN EN 10216-2:2002-08 Germany
  NiCuMoNb5-6-4 DIN EN 10216-2:2004-07 Germany
  NiCuMoNb5 Stahl Eisen List: 2000 Germany
  Diagram No.: 4551
  Type of diagram: TTT
  Mat. No. (Wr. Nr.) designation: 1.6368
  Chemical composition in weight %: 0.12% C, 0.37% Si, 0.97% Mn, 0.007% P, 0.013% S, 0.27% Cr,
  0.33% Mo, 1.12% Ni, 0.53% Cu, 0.030% Nb.
  Note: Alloy special structural steels. Austenitizing temperature: 900oC, time: 10 min.
  Source: HTDG, 2008.




Machining performance

Download 1.6368 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.