Our to produce better steel-based products are the main used in industrial manufacturing various types High temperature high strength alloy and high-temperature alloy1.4911 plate,1.4911 Round Bar,1.4911 forgings,1.4911 suppliers, 1.4911 Stock,1.4911 sheet, 1.4911 flat bar, 1.4911 pipe,1.4911 tube,1.4911 mould,1.4911 round ingot,1.4911 cold-rolled steel,1.4911 coil,1.4911 strap steel,1.4911 hot-rolled steel,1.4911 medium plate, 1.4911 heavy plate,1.4911 shapped bar,1.4911 hexahedral bar,1.4911,1.4911 slab ingot,1.4911 slab,1.4911 price,1.4911 square bar,1.4911 square steel,1.4911 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 1.4911.

Current Location:Home » Products » High temperature high strength alloy and high-temperature alloy » 1.4911

Product category

1.4911

Data Table for:Products: High temperature high strength alloy and high-temperature alloy:1.4911

1.4911 properties and heat treatment forged piece, Including 1.4911 application and specifications, We have all specifications,Including 1.4911 steel plate, 1.4911 sheet, 1.4911 square steel, 1.4911 flat bar,1.4911 round bar,1.4911 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 1.4911 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 1.4911 and Standards

X8CrCoNiMo10-6 ( 1.4911 )

Grade :     X8CrCoNiMo10-6
    Number:     1.4911
    Standard: EN 10302 : 2008   Creep resisting steels, nickel and cobalt alloys
    Classification:     Martensitic steels

Chemical composition % of the ladle analysis   of grade   X8CrCoNiMo10-6 (1.4911)




Machining performance

Download 1.4911 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.