1.4582 1.4583 1.4586 1.4911 Stainless Steel
1.4582 1.4583 1.4586 1.4911 Stainless Steel properties and heat treatment forged piece, Including 1.4582 1.4583 1.4586 1.4911 Stainless Steel application and specifications, We have all specifications，Including 1.4582 1.4583 1.4586 1.4911 Stainless Steel steel plate, 1.4582 1.4583 1.4586 1.4911 Stainless Steel sheet, 1.4582 1.4583 1.4586 1.4911 Stainless Steel square steel, 1.4582 1.4583 1.4586 1.4911 Stainless Steel flat bar,1.4582 1.4583 1.4586 1.4911 Stainless Steel round bar,1.4582 1.4583 1.4586 1.4911 Stainless Steel forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the 1.4582 1.4583 1.4586 1.4911 Stainless Steel has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade 1.4582 1.4583 1.4586 1.4911 Stainless Steel and Standards
The company is a sales and processing of integrated enterprise, there are 5,000 kinds of imported materials, such as tool steel, structural steel, carbon steel, powdered steel, high speed steel, tungsten steel (alloy steel), chromium steel, chromium molybdenum alloy steel, heat-resistant steel, stainless steel, tensile steel, bearing steel, spring steel, alloy tool steel, hot rolling plate, cold rolling double light board, gray iron, ductile iron; imported copper materials such as: Sambo copper, brass, bronze, phosphor bronze, beryllium copper, tungsten, copper, glass disabilities copper, tin bronze, phosphor copper, tin, tungsten copper, tin and zinc, copper, foreign white copper, chromium zirconium copper, zirconium bronze, chromium copper, aluminum bronze, on aluminum, Alcoa South Korea aluminum; pipes such as: straight seam pipe, carbon steel, stainless steel, aluminum, brass, pipe, structural steel, high speed steel, heat-resistant steel, tool steel, free cutting steel, boiler steel, spring steel, die steel, special steel, red brass, carbon nanotubes, carbon structural steel, high temperature alloy steel tube, bearing steel, aluminum pipe, alloy structural steel, copper alloy tube, titanium pipe, steel pipe, high-speed tool steel, alloy tool steel ; all product quality assurance, price concessions, our 24-hour free fast delivery, welcome to the needs of friends, to inquire, the Company will be happy to help you.
Machining performance
Download 1.4582 1.4583 1.4586 1.4911 Stainless Steel the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.